SANDVIK steel externally hardened by means of an exclusive high-temperature vacuum plasma process that achieves a hardness of around 60 HRC without compromising the resistance to bending of the rod | Completely nuanced finish to avoid shine | Sealing O-ring of the series winglet (red color) | Reinforced wishbone socket with curved machining radius that makes it almost impossible for the rod to break through this traditionally weak point | Versatile design for metallic and Dyneema wishbones | Extraordinary resistance to breakage in the opening direction of the notch of 190Nw and 40º of angle | Specially resistant and highly penetrating shell-shaped tip | Available diameters: Ø6.25 mm, Ø6.50 mm and Ø6.70 mm | Measurements: 90, 105, 110, 115, 120, 125, 130, 135, 140, 150 cm (depending on diameter).

Made with very strict parameters of finishes and dimensions for maximum adaptation to all types of mechanisms.
Machining carried out with hard metal stainless tools to avoid contamination of the rod material and possible rust spots in the machined areas.
Pre-stretched SANDVIK steel, externally hardened using a unique high-temperature vacuum plasma process. This process ensures that the external hope achieves a hardness of around 60 HRC without harming the resistance to bending of the rod.
The combination of steel and treatment makes the specific weight of Plasma rods 12% higher than that of the steel traditionally used in rods, in such a way that we obtain performance in terms of mass, reach and penetration equivalent to rods with a larger diameter. , with a clearly superior hydrodynamics. As an example, a Ø6.70 Plasma rod is equivalent to a Ø7.20 AISI630 or 17-4PH steel rod.
Very strict control process (rod by rod prior to machining) to check the perfect straightness of the rod.
AISI 301 stainless steel spring winglet 0.8 mm thick. Mechanical resistance 1269 Nw/mm2 close to that of the rod itself. Pin and hole proportionate to the diameter of the rod between 2 and 2.5 mm. Length in proportion to the rod; 55 mm in sizes from 90 to 120 cm, and 70 mm from 130 to 150 cm. Two-volume winglet, studied for maximum hydrodynamic penetration. Assembly with a slight recess of 1 cm in length that integrates the rivets into the profile and significantly improves the reach of the rod. The recess does not imply a decrease in resistance since the wing pin is proportioned according to the diameter of the rod. O-ring for sealing the standard winglet (red color).
Reinforced wishbone notch with curved machining radius that makes it almost impossible for the rod to break through this traditionally weak point. Versatile design for metal and Dyneema shells (we recommend polishing the profiles with a steel cable for this use). Its design, together with the parameters used for tempering, achieve an extraordinary resistance to breakage in the opening direction of the notch of 190 Nw and 40º of angle.
Specially resistant and highly penetrating bullet-shaped tip.
Locking system of the flap once it is open to ensure the capture of the piece once it has passed through.
Available diameters: Ø6.25 mm Ø6.50 mm and Ø6.70 mm.
Measurements: 90, 100, 105, 110, 115, 120, 125, 130, 135, 140, 150 cm (depending on version).
Descriptive removable paper label indicating diameter, size, reference, EAN and technical details.