TEROSON UP 130 sealing putty

Universal spatula for emergency repairs, resistant to oil, water, most common chemicals and high temperatures

Suitable for the following repairs: Gas tanks, refrigerators, concrete, Housing and castings and many others

Suitable for the following surfaces: steel, aluminium, galvanized steel, fiberglass, copper and tin

The mixture (component A + B)

Mixing ratio 100: 2-3

dripping time (20 °C, 50% RH) 4.5 min.

Sanding properties after 15 to 20 min.

preparation

The spachtelnde to substrate must be free of grease, clean and dry

In this rust has to be removed and then the corresponding

sanding repair area with 120 grit sandpaper

The paint around the repair site does not have to be removed once the existing paint has good adhesion.

The repair area is recommended to be cleaned before the next operation with TEROSON VR 20 and pretreated.

Prosecution

The filler in the volume ratio (polyester resin to TEROSON UP 190 hardener) Golf ball size (40 ml) to pea size 4 to 5 cm (2 to 3%) of the mixture until it is achieves a homogeneously mixed mass

After mixing, the drip time is approximately 4.5 minutes at 20°C.

Filler mixture is so, it is applied to the repair area that dent, scratches or surface irregularities are completed

high coating thickness must be configured to avoid cracking in several operations

The putty is sanded at room temperature after 15 to 20 minutes. accelerated curing by heat is 10 minutes after the work is possible (at a maximum of 60 ° C by IR lamps or in an oven)

Content: 739g